Carbon steels for drawing, wires, P.C. wire and mechanical springs

They consist of steels used in many industrial applications and can be subjected to reduced or high percentages of drawability and have suitable surfaces for subsequent galvanic treatments. Our casting techniques guarantee restricted analytical dispersions, low concentration of S and P, non-metallic inclusion content and controlled axial segregation of the carbon. Careful control of the rolling and cooling parameters (Stelmor bed) guarantees the achievement of the mechanical characteristics and the degree of drawability required by customers.

Mid-high carbon drawing

Steel grade

Steel grade Corresponding standard Average chemical composition
Werkstoff ORI Martin C Mn Si Cr V
C C60D2 1.1228 MC6001 0,60 0,60 0,20 - -
C68D2 1.1232 MC6801 0,68 0,60 0,20 - -
C70D2 1.1251 MC7201 0,70 0,60 0,20 - -
C80D2 1.1255 MC8201 0,80 0,60 0,20 - -
C86D2 1.1265 MC8501 0,86 0,60 0,20 - -
C92D2 1.1282 MC9201 0,93 0,60 0,20 - -
Cr C80+Cr MC8001 0,80 0,60 0,20 0,20 -
Cr V C80+CrV MC8002 0,82 0,75 0,22 0,25 0,07
Download

Products



ORI Martin S.p.A.
Wire rod

Rolling takes place at a controlled temperature using the very latest technology. This allows a smaller grain size to be obtained together with a more fine and even structure. Optimal characteristics for subsequent use in drawing and cold moulding in addition to a higher degree of globularisation after the annealing process.

Sales

Alberto Franchi

Export Sales Manager

Italy

Phone +39 030 3999 205

Alessandro Lombardi

Sales Manager Italy

Italy

Phone +39 030 3999 214

Alberto Petroboni

Sales Manager Italy

Italy

Phone +39 030 3999 272

Julia Seeber

Export Sales

Italy

Phone +39 030 3999 224


ORI Martin France Sarl

Sales

Michel Pham

France

Phone +33 3 873 610 90


ORI Martin Deutschland GmbH

Sales

Mario Gerth

Sales manager

Germany

Phone +49 203 318 77 16


Siderurgica Latina Martin S.p.A.
PC Strand - 7 wire

PC Strand consists of a group of seven cold drawn wires having a central wire (core wire) around which are helically spun six wires in one layer and with uniform pitch. PC Strand is mostly intended  for the construction industries to produce precast concrete elements, rock & soil anchors, concrete poles as well as for pre-stressing and post-tensioning applications.

PC Strand - 2&3 wire

Established in 1963, Siderurgica Latina Martin focuses on manufacturing PC Strand (2 & 3 wires) in accordance with the most recognized international standards.
Siderurgica Latina Martin turns High Carbon Wire Rod into PC Strand (2 & 3 wires) through an integrated manufacturing process starting from in-house Acid Pickling & Pre-Coating, Cold Wire Drawing, Stranding, Thermo-Mechanical Process to Rewinding & Packaging.

2 & 3 Wire Strand consists of a group of 2 & 3 high tensile strength cold drawn wires spun together in helical form over a theoretical common axis in one layer with uniform pitch.
2 & 3 Wire Strand is widely used in precast concrete elements and concrete poles.
Additional configurations of 2 & 3 wire PC Strand can be produced on demand.

Diameter Range: 2-wires: 4,50 mm | 3-wires: 4,85 mm to 8,60 mm
Tensile Strength Range: 1770 Mpa to 2160 Mpa
Coil Weight: 190 kg to 3.000 kg

PC wire

PC Wire is supplied either  smooth or indented and it  is packed and delivered either in coils or in bundle of straight  cut-to-length bars. PC Wire in straight cut-to-length bar is used to produce railroad sleepers whereas PC Wire in coils is mostly used as reinforcement in concrete pre-stressed elements.

Medium-High carbon wire

Drawn wire is produced in the SLM facility for medium to high carbon springs for applications in the mechanical spring sector. 
Diameter Range: Ø from 1,30 mm up to 12,00 mm